In this paper, an intumescent flame retardant treatment, obtained by a combination of vinylphosphonic acid (VPA) and methacrylamide (MAA), was applied to cotton fabrics. In order to improve the cross-linking degree onto cellulose polymers, potassium persulfate was used as initiator of a radical polymerization technique. The application on cotton was carried out by padding, followed by drying and a curing treatment. The treated samples were characterized by SEM, TGA and FTIR-ATR analyses and tested in terms of flammability and washing fastness. The thermal and fire behavior of the treated fabrics was thoroughly investigated. The results clearly showed that the VPA/MAA coating was able to exert a protective action, giving rise to the formation of a stable char on the surface of textile fibers upon heating, hence improving the flame retardant performance of cotton. Horizontal flame spread tests confirmed that the coated fabrics achieved self-extinction, and the residues well preserved the original weave structure and fiber morphology; at variance, the uncoated fabric left only ashes. A remarkable weight loss was observed only after the first washing cycle, then the samples did not show any significant weight loss, hence confirming the durability of the self-extinguishing treatment, even after five laundering cycles.

(2017). Intumescent flame retardant properties of graft copolymerized vinyl monomers onto cotton fabric . In IOP CONFERENCE SERIES: MATERIALS SCIENCE AND ENGINEERING. Retrieved from http://hdl.handle.net/10446/112201

Intumescent flame retardant properties of graft copolymerized vinyl monomers onto cotton fabric

Rosace, G.;Trovato, V.;
2017-01-01

Abstract

In this paper, an intumescent flame retardant treatment, obtained by a combination of vinylphosphonic acid (VPA) and methacrylamide (MAA), was applied to cotton fabrics. In order to improve the cross-linking degree onto cellulose polymers, potassium persulfate was used as initiator of a radical polymerization technique. The application on cotton was carried out by padding, followed by drying and a curing treatment. The treated samples were characterized by SEM, TGA and FTIR-ATR analyses and tested in terms of flammability and washing fastness. The thermal and fire behavior of the treated fabrics was thoroughly investigated. The results clearly showed that the VPA/MAA coating was able to exert a protective action, giving rise to the formation of a stable char on the surface of textile fibers upon heating, hence improving the flame retardant performance of cotton. Horizontal flame spread tests confirmed that the coated fabrics achieved self-extinction, and the residues well preserved the original weave structure and fiber morphology; at variance, the uncoated fabric left only ashes. A remarkable weight loss was observed only after the first washing cycle, then the samples did not show any significant weight loss, hence confirming the durability of the self-extinguishing treatment, even after five laundering cycles.
2017
Rosace, Giuseppe; Colleoni, C.; Trovato, Valentina; Iacono, G.; Malucelli, G.
File allegato/i alla scheda:
File Dimensione del file Formato  
2017 Intumescent flame retardant properties of graft copolymerized vinyl monomers onto cotton fabric.pdf

accesso aperto

Versione: publisher's version - versione editoriale
Licenza: Creative commons
Dimensione del file 464.49 kB
Formato Adobe PDF
464.49 kB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/112201
Citazioni
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 1
social impact