This work focuses on the fatigue behaviour of notched Ti-6Al-4V titanium alloy in inert environment. V-notched flat samples were cycled under axial fatigue (R = 0.1) under inert conditions by immersion in paraffin oil. A step-loading technique was used to determine the fatigue limit at the complete fracture for a constant fatigue life of 2×105 load cycles. The results were compared with previous data obtained with tests carried out in air and 3.5 wt.% NaCl solution. Fracture surfaces were examined under stereoscopic microscope.

(2012). Fatigue behavior of notched Ti-6Al-4V in inert environment [conference presentation - intervento a convegno]. Retrieved from http://hdl.handle.net/10446/28229

Fatigue behavior of notched Ti-6Al-4V in inert environment

Baragetti, Sergio;Cavalleri, Stefano;Tordini, Federico
2012-01-01

Abstract

This work focuses on the fatigue behaviour of notched Ti-6Al-4V titanium alloy in inert environment. V-notched flat samples were cycled under axial fatigue (R = 0.1) under inert conditions by immersion in paraffin oil. A step-loading technique was used to determine the fatigue limit at the complete fracture for a constant fatigue life of 2×105 load cycles. The results were compared with previous data obtained with tests carried out in air and 3.5 wt.% NaCl solution. Fracture surfaces were examined under stereoscopic microscope.
2012
Baragetti, Sergio; Cavalleri, Stefano; Tordini, Federico
File allegato/i alla scheda:
File Dimensione del file Formato  
baragetti2011.pdf

Solo gestori di archivio

Versione: publisher's version - versione editoriale
Licenza: Licenza default Aisberg
Dimensione del file 1.09 MB
Formato Adobe PDF
1.09 MB Adobe PDF   Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/28229
Citazioni
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 2
social impact