The paper reports on the corrosion behavior of two aluminum alloys, with different silicon content, manufactured by means of laser powder bed fusion. The results of potentiodynamic tests and intergranular corrosion tests are discussed in order to evaluate the effect of film formed during manufacturing and successive stress relieving and plane orientation. The results show on both alloys the propagation of localized attack by selective dissolution of aluminum along borders of melt pool. A clear reduction of pitting potential was recognized on the surface as produced by the manufacturing process and less marked variations between different planes. The tests did not reveal a systematic variation of the pitting potential between the two alloys.

Il lavoro è volto allo studio del comportamento alla corrosione di due leghe di alluminio-silicio tipo AlSi7Mg e AlSi10Mg, prodotte per fusione laser a letto di polvere. Sono state effettuate prove elettrochimiche potenziodinamiche e prove di corrosione intergranulare su campioni accresciuti lungo due diverse direzioni (su piani paralleli a quello di scansione del laser e perpendicolari a questo), sia sulla superficie così come ottenuta dal processo produttivo sia dopo lucidatura. Per entrambe le leghe, la morfologia di attacco localizzato è caratterizzata da una dissoluzione selettiva dell’alluminio al bordo del pozzetto di fusione. Il potenziale di pitting aumenta in modo considerevole passando dalla superficie così come prodotta dal processo alla superficie lucidata. Sebbene in misura inferiore, aumenta anche passando dalle superfici con giacitura perpendicolare a quella di scansione alle superfici parallele a questa, a causa della diversa microstruttura. Le prove non hanno evidenziato una variazione sistematica del potenziale di pitting tra le due leghe.

(2017). Evaluation of corrosion resistance of aluminum silicon alloys manufactured by LPBF [journal article - articolo]. In LA METALLURGIA ITALIANA. Retrieved from http://hdl.handle.net/10446/116554

Evaluation of corrosion resistance of aluminum silicon alloys manufactured by LPBF

Cabrini, Marina;Lorenzi, Sergio;Pastore, Tommaso;Pellegrini, Simone;Testa, Cristian;Manfredi, Diego;
2017-07-01

Abstract

The paper reports on the corrosion behavior of two aluminum alloys, with different silicon content, manufactured by means of laser powder bed fusion. The results of potentiodynamic tests and intergranular corrosion tests are discussed in order to evaluate the effect of film formed during manufacturing and successive stress relieving and plane orientation. The results show on both alloys the propagation of localized attack by selective dissolution of aluminum along borders of melt pool. A clear reduction of pitting potential was recognized on the surface as produced by the manufacturing process and less marked variations between different planes. The tests did not reveal a systematic variation of the pitting potential between the two alloys.
journal article - articolo
lug-2017
Il lavoro è volto allo studio del comportamento alla corrosione di due leghe di alluminio-silicio tipo AlSi7Mg e AlSi10Mg, prodotte per fusione laser a letto di polvere. Sono state effettuate prove elettrochimiche potenziodinamiche e prove di corrosione intergranulare su campioni accresciuti lungo due diverse direzioni (su piani paralleli a quello di scansione del laser e perpendicolari a questo), sia sulla superficie così come ottenuta dal processo produttivo sia dopo lucidatura. Per entrambe le leghe, la morfologia di attacco localizzato è caratterizzata da una dissoluzione selettiva dell’alluminio al bordo del pozzetto di fusione. Il potenziale di pitting aumenta in modo considerevole passando dalla superficie così come prodotta dal processo alla superficie lucidata. Sebbene in misura inferiore, aumenta anche passando dalle superfici con giacitura perpendicolare a quella di scansione alle superfici parallele a questa, a causa della diversa microstruttura. Le prove non hanno evidenziato una variazione sistematica del potenziale di pitting tra le due leghe.
Cabrini, Marina; Lorenzi, Sergio; Pastore, Tommaso; Pellegrini, Simone; Testa, Cristian; Manfredi, Diego Giovanni; Calignano, F.; Fino, P.; Cattano, G...espandi
(2017). Evaluation of corrosion resistance of aluminum silicon alloys manufactured by LPBF [journal article - articolo]. In LA METALLURGIA ITALIANA. Retrieved from http://hdl.handle.net/10446/116554
File allegato/i alla scheda:
File Dimensione del file Formato  
metallurgia italiana_17.pdf

Solo gestori di archivio

Versione: publisher's version - versione editoriale
Licenza: Licenza default Aisberg
Dimensione del file 1 MB
Formato Adobe PDF
1 MB Adobe PDF   Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/116554
Citazioni
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 5
social impact