In this paper the fatigue behaviour of Ti-6Al-4V alloy coated with a TiN arc-deposited PVD film was studied. Rotating bending tests (R = -1) were carried out on standard “hourglass” specimens to evaluate the fatigue limit at 200000 load cycles. Conventional and notched (120° Vnotch transversal to the rotating axis at the minimum cross section area) specimens were tested, both coated and uncoated, to investigate the effect of the coating on the fatigue limit of the titanium alloy, with and without the surface notch. Fracture surfaces were observed by SEM. The coating did not improve the titanium alloy fatigue life.

(2007). Fatigue behaviour of notched PVD-coated titanium components [conference presentation - intervento a convegno]. Retrieved from http://hdl.handle.net/10446/21382

Fatigue behaviour of notched PVD-coated titanium components

BARAGETTI, Sergio;TORDINI, Federico
2007-01-01

Abstract

In this paper the fatigue behaviour of Ti-6Al-4V alloy coated with a TiN arc-deposited PVD film was studied. Rotating bending tests (R = -1) were carried out on standard “hourglass” specimens to evaluate the fatigue limit at 200000 load cycles. Conventional and notched (120° Vnotch transversal to the rotating axis at the minimum cross section area) specimens were tested, both coated and uncoated, to investigate the effect of the coating on the fatigue limit of the titanium alloy, with and without the surface notch. Fracture surfaces were observed by SEM. The coating did not improve the titanium alloy fatigue life.
2007
Lusvarghi, Luca; Baragetti, Sergio; PIGHETTI MANTINI, Fabio; Tordini, Federico
File allegato/i alla scheda:
Non ci sono file allegati a questa scheda.
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/21382
Citazioni
  • Scopus 14
  • ???jsp.display-item.citation.isi??? 10
social impact