The results of 2-chloroaniline (2-CA) immobilization experiments in cement matrices, using an organophilic clay modified with phenolic resins as pre-sorbent, are shown. The 2-CA suspended in water was kept in contact with the organoclay for 24 hours, and the slurry obtained was then admixed with ordinary Portland cement (OPC) without additional water, to obtain a firm solid waste. Six cement-clay pastes were prepared with the same water-to-cement ratio (0.50 wt/wt), but with different slurry composition (water-to-organoclay ratio equal to 10 and 5 wt/wt, respectively) and different amounts of 2-CA suspended in water, i.e. 5000, 15000, and 25000 ppmw (weight). Dynamic leach tests were performed on solidified monoliths in order to assess the successful immobilization of the 2-CA. Moreover, X-ray diffraction (XRD), scanning electron microscopy (SEM-EDS) and infrared spectroscopy (FTIR) analyses were carried out.

Immobilization of organic pollutants in cement pastes admixed with organophilic materials

NATALI SORA, Isabella;PELOSATO, Renato
2008-01-01

Abstract

The results of 2-chloroaniline (2-CA) immobilization experiments in cement matrices, using an organophilic clay modified with phenolic resins as pre-sorbent, are shown. The 2-CA suspended in water was kept in contact with the organoclay for 24 hours, and the slurry obtained was then admixed with ordinary Portland cement (OPC) without additional water, to obtain a firm solid waste. Six cement-clay pastes were prepared with the same water-to-cement ratio (0.50 wt/wt), but with different slurry composition (water-to-organoclay ratio equal to 10 and 5 wt/wt, respectively) and different amounts of 2-CA suspended in water, i.e. 5000, 15000, and 25000 ppmw (weight). Dynamic leach tests were performed on solidified monoliths in order to assess the successful immobilization of the 2-CA. Moreover, X-ray diffraction (XRD), scanning electron microscopy (SEM-EDS) and infrared spectroscopy (FTIR) analyses were carried out.
journal article - articolo
2008
Zampori, Luca; GALLO STAMPINO, Paola; Dotelli, Giovanni; NATALI SORA, Isabella; Pelosato, Renato
File allegato/i alla scheda:
Non ci sono file allegati a questa scheda.
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/21703
Citazioni
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 2
social impact