Potentiodynamic and potentiostatic polarization tests were performed in an aerated chloride solution on specimens laser powder bed fusion printed with different building platform temperatures. Potentiodynamic polarization tests showed two break-down potentials for the polished specimens. The first was associated with the initiation of corrosion localized on the edge of the melting pool, while the second with the breakage of the passive film of the matrix. On the specimens with the surface as built, these two potentials are practically superimposed and lower than the respective polished specimens. No differences were observed between the breakdown potentials of the specimens as a function of the temperature of the building platform, while the time to trigger the selective attack in the potentiostatic tests increases as the plate temperature decreases.

Sono state eseguite prove di polarizzazione potenziodinamica e potenziostatica in soluzione aerata di cloruri su provini stampati con diverse temperature della piastra. Le prove di polarizzazione potenziodinamica hanno evidenziato per i provini lucidati, due potenziali di break-down. Il primo è stato associato all’innesco della corrosione localizzata sul bordo del pozzetto di fusione, mentre il secondo alla rottura del film passivo della matrice. Sui provini con superficie tal quale questi due potenziali sono praticamente sovrapposti e decisamente inferiori rispetto ai rispettivi provini lucidati. Non sono state osservate differenze tra i potenziali di breakdown dei provini in funzione della temperatura della piastra, mentre i tempi di innesco dell’attacco nelle prove potenziostatiche crescono al diminuire della temperatura della piastra.

(2022). Effetto della temperatura di piastra sulla corrosione localizzata della lega AlSi10Mg ottenuta per Laser Powder Bed Fusion [journal article - articolo]. In LA METALLURGIA ITALIANA. Retrieved from https://hdl.handle.net/10446/232234

Effetto della temperatura di piastra sulla corrosione localizzata della lega AlSi10Mg ottenuta per Laser Powder Bed Fusion

Cabrini, Marina;Lorenzi, Sergio;Pastore, Tommaso
2022-01-01

Abstract

Sono state eseguite prove di polarizzazione potenziodinamica e potenziostatica in soluzione aerata di cloruri su provini stampati con diverse temperature della piastra. Le prove di polarizzazione potenziodinamica hanno evidenziato per i provini lucidati, due potenziali di break-down. Il primo è stato associato all’innesco della corrosione localizzata sul bordo del pozzetto di fusione, mentre il secondo alla rottura del film passivo della matrice. Sui provini con superficie tal quale questi due potenziali sono praticamente sovrapposti e decisamente inferiori rispetto ai rispettivi provini lucidati. Non sono state osservate differenze tra i potenziali di breakdown dei provini in funzione della temperatura della piastra, mentre i tempi di innesco dell’attacco nelle prove potenziostatiche crescono al diminuire della temperatura della piastra.
articolo
Potentiodynamic and potentiostatic polarization tests were performed in an aerated chloride solution on specimens laser powder bed fusion printed with different building platform temperatures. Potentiodynamic polarization tests showed two break-down potentials for the polished specimens. The first was associated with the initiation of corrosion localized on the edge of the melting pool, while the second with the breakage of the passive film of the matrix. On the specimens with the surface as built, these two potentials are practically superimposed and lower than the respective polished specimens. No differences were observed between the breakdown potentials of the specimens as a function of the temperature of the building platform, while the time to trigger the selective attack in the potentiostatic tests increases as the plate temperature decreases.
Cabrini, Marina; Lorenzi, Sergio; Pastore, Tommaso
(2022). Effetto della temperatura di piastra sulla corrosione localizzata della lega AlSi10Mg ottenuta per Laser Powder Bed Fusion [journal article - articolo]. In LA METALLURGIA ITALIANA. Retrieved from https://hdl.handle.net/10446/232234
File allegato/i alla scheda:
File Dimensione del file Formato  
metallurgia italiana 22_AlSi10Mg.pdf

Solo gestori di archivio

Versione: publisher's version - versione editoriale
Licenza: Licenza default Aisberg
Dimensione del file 1.24 MB
Formato Adobe PDF
1.24 MB Adobe PDF   Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/232234
Citazioni
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact