Valutazione dell’effetto dell’aggiunta di argilla sull’effetto barriera di rivestimenti epossidici per la protezione dalla corrosione

The paper deals with the study on Cloisite30B® nano-clay addition for enhancing corrosion protection properties of polymer matrix coatings to improve service life of carbon steel structures. The effect of additions up to 5 % Cloisite 30B® on the barrier properties of an epoxy-based system was evaluated. Different tests were performed on low-thickness spe cimens (35-55 μm) coated by hand lay-up technique. Preliminary test was conducted for measuring surface roughness and by IR analysis to verify the effects of filler on the cross-linking of the polymer matrix. Electrochemical impedance spectroscopy (EIS) tests were carried out in aerated sodium chloride solution up to 2 to 1000 h exposure. The results show a positive effect for additions of 1% Cloisite 30B®.

L’articolo è volto allo studio dell’impiego dell’argilla commerciale Cloisite30B® per lo sviluppo di rivestimenti a matri ce polimerica con doti migliori di protezione dalla corrosione, in grado di incrementare la vita di servizio delle strutture in acciaio al carbonio. Si sono valutate aggiunte fino al 5 % sulle proprietà barriera di un sistema a base epossidica. Le prove sono state eseguite su provini rivestiti con la tecnica hand lay up, a basso spessore (35-55 μm). Sono state effettuate analisi preliminari di rugosità della superficie e di spettroscopia IR per valutare l’effetto delle particelle sulla reticolazione della matrice polimerica. Sono state effettuate prove di spettroscopia di impedenza elettrochimica (EIS) in soluzione di cloruro di sodio aerata dopo diversi tempi di immersione, da 2 a 1000 h di esposizione, per evidenziare l’evoluzione delle proprietà di barriera. I risultati dimostrano un effetto positivo di aggiunte di 1% di Cloisite 30B®.