Advanced researches on concrete are directed toward investigating the behavior of reinforced concrete structures in severe conditions such as those promoted by impact loads. Some particular structures (protective shelters, nuclear reactor containment, offshore structures, military structures, chemical or Energy production plant) may be subjected to loading at very high rate of stress or strain caused by impact of missiles or flying objects, also by vehicle collisions or impulses due to explosions and earthquakes. Resistance to impact loads is guaranteed by using cementitious materials having both high strength and ductility. In order to improve ductility cementitious mortars with Glass Reinforced Plastics (GRP) replacing partially the natural sand were manufactured. Moreover, glass fiber (GF) reinforced mortars were produced to enhance toughness. For this scope two types of glass fibers were used different in length and diameter. Since the use of GRP and GF don’t produce any increase in strength of the mortars Carbon Nanotubes were added in the cement matrix to enhance tensile strength of the cementitious composite. Flexural, compressive and Hopkinson bar tests were carried out to evaluate the role of the different materials used. Replacing partially the natural sand with Glass Reinforced Plastics (GRP), compressive and flexural strength decrease (about 20%) with respect those of the reference mortar both on static and dynamic condition as a consequence of an anomalous air entrapment. Adding glass fibers (GF), GRP or/and Carbon Nanotubes (CNTs) no substantial improvement in terms of mechanical properties under static condition was occurred. The Dynamic Increase Factor of the reference mortar was higher than that of the reinforced mixtures, but fracture energy was lower. In particular, combined addition of carbon nanotubes and GRP determines an increase in the energy fracture. The higher the carbon nanotubes content, the higher both fracture energy and tensile strength because nanoparticles oppose to wave and crack propagation, increasing the high strain rate strength. GRP and CNTs reinforced mortars need more fracture energy to failure at 150 s-1 strain rate.

(2011). Mechanical Characterization of Cement Composites Reinforced with Fiberglass, Carbon Nanotubes or Glass Reinforced Plastic (GRP) at High Strain Rates [conference presentation - intervento a convegno]. Retrieved from http://hdl.handle.net/10446/26361

Mechanical Characterization of Cement Composites Reinforced with Fiberglass, Carbon Nanotubes or Glass Reinforced Plastic (GRP) at High Strain Rates

COPPOLA, Luigi;BUOSO, Alessandra;
2011-01-01

Abstract

Advanced researches on concrete are directed toward investigating the behavior of reinforced concrete structures in severe conditions such as those promoted by impact loads. Some particular structures (protective shelters, nuclear reactor containment, offshore structures, military structures, chemical or Energy production plant) may be subjected to loading at very high rate of stress or strain caused by impact of missiles or flying objects, also by vehicle collisions or impulses due to explosions and earthquakes. Resistance to impact loads is guaranteed by using cementitious materials having both high strength and ductility. In order to improve ductility cementitious mortars with Glass Reinforced Plastics (GRP) replacing partially the natural sand were manufactured. Moreover, glass fiber (GF) reinforced mortars were produced to enhance toughness. For this scope two types of glass fibers were used different in length and diameter. Since the use of GRP and GF don’t produce any increase in strength of the mortars Carbon Nanotubes were added in the cement matrix to enhance tensile strength of the cementitious composite. Flexural, compressive and Hopkinson bar tests were carried out to evaluate the role of the different materials used. Replacing partially the natural sand with Glass Reinforced Plastics (GRP), compressive and flexural strength decrease (about 20%) with respect those of the reference mortar both on static and dynamic condition as a consequence of an anomalous air entrapment. Adding glass fibers (GF), GRP or/and Carbon Nanotubes (CNTs) no substantial improvement in terms of mechanical properties under static condition was occurred. The Dynamic Increase Factor of the reference mortar was higher than that of the reinforced mixtures, but fracture energy was lower. In particular, combined addition of carbon nanotubes and GRP determines an increase in the energy fracture. The higher the carbon nanotubes content, the higher both fracture energy and tensile strength because nanoparticles oppose to wave and crack propagation, increasing the high strain rate strength. GRP and CNTs reinforced mortars need more fracture energy to failure at 150 s-1 strain rate.
2011
Coppola, Luigi; Cadoni, Ezio; Buoso, Alessandra; Forni, Daniele
File allegato/i alla scheda:
File Dimensione del file Formato  
146.pdf

accesso aperto

Descrizione: author's postprint - versione referata
Dimensione del file 367.88 kB
Formato Adobe PDF
367.88 kB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/26361
Citazioni
  • Scopus 42
  • ???jsp.display-item.citation.isi??? 30
social impact