In the present experimental work, a WC/C coated 7075-T6 aluminum alloy was considered from the corrosion point of view. The coating was deposited by PVD technique with a final thickness of about 2.5mm. In order to study the influence of the coating on the corrosion behavior of the aluminum alloy, the samples surfaces were partially coated and the interface among the metal and the coating was analyzed after the corrosion tests described into the ASTM G110 standard. Such experimental plan was decided in order to simulate the possible in-service local removal of the thin and hard coating. This kind of damage, due for example to a foreign object impact, can occur because of the great hardness difference between the coating and the substrate. The experimental tests were carried out on samples with different surface finishing, ranging from about 0.02mm Ra (mirror-polished surface) to about 0.8mm Ra (320 grit paper). The aim of such choice was to investigate the effect of a surface roughness different from the optimal one (mirror polished) on the coating deposition. Moreover a different corrosion resistance is expected.

(2013). Corrosion behavior of a WC/C Coated 7075-T6 Aluminum Alloy [conference presentation - intervento a convegno]. Retrieved from http://hdl.handle.net/10446/29966

Corrosion behavior of a WC/C Coated 7075-T6 Aluminum Alloy

BARAGETTI, Sergio;
2013-01-01

Abstract

In the present experimental work, a WC/C coated 7075-T6 aluminum alloy was considered from the corrosion point of view. The coating was deposited by PVD technique with a final thickness of about 2.5mm. In order to study the influence of the coating on the corrosion behavior of the aluminum alloy, the samples surfaces were partially coated and the interface among the metal and the coating was analyzed after the corrosion tests described into the ASTM G110 standard. Such experimental plan was decided in order to simulate the possible in-service local removal of the thin and hard coating. This kind of damage, due for example to a foreign object impact, can occur because of the great hardness difference between the coating and the substrate. The experimental tests were carried out on samples with different surface finishing, ranging from about 0.02mm Ra (mirror-polished surface) to about 0.8mm Ra (320 grit paper). The aim of such choice was to investigate the effect of a surface roughness different from the optimal one (mirror polished) on the coating deposition. Moreover a different corrosion resistance is expected.
2013
Baragetti, Sergio; Daurú, Mauro; Gerosa, Riccardo; Rivolta, Barbara
File allegato/i alla scheda:
File Dimensione del file Formato  
KEM-PUBLISHED-BARAGETTI-GEROSA-DAURU-RIVOLTA-2014.pdf

accesso aperto

Descrizione: publisher's version - versione dell'editore
Dimensione del file 581.97 kB
Formato Adobe PDF
581.97 kB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/29966
Citazioni
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact