The fatigue behavior of AA6060-T6 friction stir welded butt joints was investigated. The joints were produced by using both a standard and a threaded tri-flute cylindrical-tool with flat shoulder. The friction stir welding process was carried out using different feed rates. Preliminary tensile tests, micrograph analyses and hardness profile measurements across the welds were carried out. Welded and unwelded fatigue samples were tested under axial loading (R = 0.1) with upper limits of 104 and 105 cycles, using threaded and unthreaded (standard) tools at different feed rates. The best tensile and fatigue performance was obtained using the standard tool at low feed rate.
Aluminum 6060-T6 friction stir welded butt joints: fatigue resistance with different tools and feed rates
BARAGETTI, Sergio;D'URSO, Gianluca Danilo
2014-01-01
Abstract
The fatigue behavior of AA6060-T6 friction stir welded butt joints was investigated. The joints were produced by using both a standard and a threaded tri-flute cylindrical-tool with flat shoulder. The friction stir welding process was carried out using different feed rates. Preliminary tensile tests, micrograph analyses and hardness profile measurements across the welds were carried out. Welded and unwelded fatigue samples were tested under axial loading (R = 0.1) with upper limits of 104 and 105 cycles, using threaded and unthreaded (standard) tools at different feed rates. The best tensile and fatigue performance was obtained using the standard tool at low feed rate.| File | Dimensione del file | Formato | |
|---|---|---|---|
|
KSME DUrso Baragetti.pdf
Solo gestori di archivio
Versione:
publisher's version - versione editoriale
Licenza:
Licenza default Aisberg
Dimensione del file
4.81 MB
Formato
Adobe PDF
|
4.81 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo