The present work reports on the effect of constant bending load on corrosion and repassivation of high strength 2024-T3 and 7075-T6 Al alloys in NaCl solutions, investigated by means of single cycle anodic polarization and galvanic corrosion experiments. Bending loads up to the yield strength of a given alloy were applied using four point bent beam stress corrosion test specimens. The effect of bending load (side in tension) on the electrochemical behavior is more evident for Al 7075-T6, also in the presence of galvanic coupling with CRES 304. A critical electrochemical condition associated to the onset of microplasticity is identified from the repassivation behavior. The existence of such critical condition though less noticeable is indicated for Al 2024-T3 also. In this case, the effect of stress is likely overwhelmed by microstructural corrosion. Overall results emphasize the interdependence between the local aggressive environment, the electrochemical event and the mechanical state in the stress corrosion cracking of Al alloys.

Con il presente lavoro si riporta l’effetto dell’applicazione di una condizione di sollecitazione a flessione sui meccanismi di corrosione e ripassivazione delle leghe di alluminio 2024-T3 e 7075-T6 in soluzioni aggressive di NaCl, investigati tramite polarizzazione anodica a singolo ciclo ed esperimenti di corrosione galvanica. Sono stati applicati carichi fino al raggiungimento della tensione di snervamento di ogni specifica lega utilizzando provini di tensocorrosione in condizione di sollecitazione a flessione su 4 punti (4PBB). L’effetto del carico a flessione (a sollecitazione costante) sul comportamento elettrochimico risulta più evidente per la lega Al 7075-T6, anche in presenza di accoppiamento galvanico con CRES 304. Una condizione elettrochimica critica, associata all’insorgenza di microplasticità, è stata identificata dal comportamento a ripassivazione. L’esistenza di tale punto critico, sebbene meno evidente, può essere indicata anche per la lega Al 2024-T3. In questo caso, l’effetto della sollecitazione meccanica è probabilmente mascherato dalla corrosione microstrutturale tipica della lega in questione (microstructural pitting), derivante dalla presenza nella stessa di intermetallici a funzione catodica ricchi in rame. I risultati complessivi sottolineano l'interdipendenza nella tensocorrosione delle leghe di Al tra ambiente aggressivo, evento elettrochimico e stato meccanico.

Effect of mechanical deformation on corrosion and repassivation of 2024-T3 and 7075-T6 aluminum alloys

CABRINI, Marina;
2016-12-01

Abstract

The present work reports on the effect of constant bending load on corrosion and repassivation of high strength 2024-T3 and 7075-T6 Al alloys in NaCl solutions, investigated by means of single cycle anodic polarization and galvanic corrosion experiments. Bending loads up to the yield strength of a given alloy were applied using four point bent beam stress corrosion test specimens. The effect of bending load (side in tension) on the electrochemical behavior is more evident for Al 7075-T6, also in the presence of galvanic coupling with CRES 304. A critical electrochemical condition associated to the onset of microplasticity is identified from the repassivation behavior. The existence of such critical condition though less noticeable is indicated for Al 2024-T3 also. In this case, the effect of stress is likely overwhelmed by microstructural corrosion. Overall results emphasize the interdependence between the local aggressive environment, the electrochemical event and the mechanical state in the stress corrosion cracking of Al alloys.
dic-2016
Con il presente lavoro si riporta l’effetto dell’applicazione di una condizione di sollecitazione a flessione sui meccanismi di corrosione e ripassivazione delle leghe di alluminio 2024-T3 e 7075-T6 in soluzioni aggressive di NaCl, investigati tramite polarizzazione anodica a singolo ciclo ed esperimenti di corrosione galvanica. Sono stati applicati carichi fino al raggiungimento della tensione di snervamento di ogni specifica lega utilizzando provini di tensocorrosione in condizione di sollecitazione a flessione su 4 punti (4PBB). L’effetto del carico a flessione (a sollecitazione costante) sul comportamento elettrochimico risulta più evidente per la lega Al 7075-T6, anche in presenza di accoppiamento galvanico con CRES 304. Una condizione elettrochimica critica, associata all’insorgenza di microplasticità, è stata identificata dal comportamento a ripassivazione. L’esistenza di tale punto critico, sebbene meno evidente, può essere indicata anche per la lega Al 2024-T3. In questo caso, l’effetto della sollecitazione meccanica è probabilmente mascherato dalla corrosione microstrutturale tipica della lega in questione (microstructural pitting), derivante dalla presenza nella stessa di intermetallici a funzione catodica ricchi in rame. I risultati complessivi sottolineano l'interdipendenza nella tensocorrosione delle leghe di Al tra ambiente aggressivo, evento elettrochimico e stato meccanico.
Ferri, Michele; Guastaferro, Daniele; Trueba, Monica; Trasatti, Stefano P.; Cabrini, Marina; Lo Conte, A.
File allegato/i alla scheda:
File Dimensione del file Formato  
Metallurgia Italiana 1.pdf

Solo gestori di archivio

Versione: publisher's version - versione editoriale
Licenza: Licenza default Aisberg
Dimensione del file 1.52 MB
Formato Adobe PDF
1.52 MB Adobe PDF   Visualizza/Apri
Pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10446/79720
Citazioni
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact