The following steels have been chosen for this work: API 5AC L80, AISI 4137H, AISI 420 - API 5AC C90, 22Cr-5. 5Ni-3Mo, 27Cr-31Ni-3. 5Mo. The tests have been performed both in NACE solution, both in modified NACE solution (in which a 90% CO//2 plus 10% H//2S gas was bubbling). Smooth and precracked specimens have been used. The impossibility of using carbon or low alloy steels at high strength levels when relevant H//2S contents are present has been confirmed.

(1984). Sulfide stress corrosion cracking in steels for the oil industry . Retrieved from http://hdl.handle.net/10446/82267

Sulfide stress corrosion cracking in steels for the oil industry

PASTORE, Tommaso;
1984

Abstract

The following steels have been chosen for this work: API 5AC L80, AISI 4137H, AISI 420 - API 5AC C90, 22Cr-5. 5Ni-3Mo, 27Cr-31Ni-3. 5Mo. The tests have been performed both in NACE solution, both in modified NACE solution (in which a 90% CO//2 plus 10% H//2S gas was bubbling). Smooth and precracked specimens have been used. The impossibility of using carbon or low alloy steels at high strength levels when relevant H//2S contents are present has been confirmed.
Cigada, Alberto; Mazza, Bruno; Pastore, Tommaso; Pedeferri, Pietro
File allegato/i alla scheda:
Non ci sono file allegati a questa scheda.
Pubblicazioni consigliate

Caricamento pubblicazioni consigliate

Aisberg ©2008 Servizi bibliotecari, Università degli studi di Bergamo | Terms of use/Condizioni di utilizzo

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/10446/82267
Citazioni
  • Scopus 1
  • ???jsp.display-item.citation.isi??? ND
social impact